Principales compétences techniques du fil en alliage nickel-chrome
Marque/Performance
Cr20Ni80
Cr30Ni70
Cr15Ni60
Cr20Ni35
Cr20Ni30
Composition chimique principale%
Ni
marge
marge
55.0～61.0
34.0～37.0
30.0～34.0
Cr
20.0～23.0
28.0～31.0
15.0～18.0
18.0～21.0
18.0～21.0
Fe
≤1.0
≤1.0
marge
marge
marge
La température d'utilisation la plus élevée du composant ℃
1200
1250
1150
1100
1100
Point de fusion °C
1400
1380
1390
1390
1390
Densité g/cm3
8.40
8.10
8.20
7.90
7.90
Résistivité μΩ·m, 20℃
1.09±0.05
1.18±0.05
1.11±0.05
1.04±0.05
1.04±0.05
Élongation%
≥20
≥20
≥20
≥20
≥20
Chaleur spécifique J/g.℃
0.440
0.461
0.494
0.500
0.500
Conductivité thermique KJ/mh℃
60.3
45.2
45.2
43.8
43.8
Coefficient de dilatation linéaire a×10-6/℃ (20～1000℃)
18.0
17.0
17.0
19.0
19.0
Microstructure
Austénite
Austénite
Austénite
Austénite
Austénite
magnétique
Non magnétique
Non magnétique
Non magnétique
Non magnétique
Non magnétique
Principaux paramètres de conception du fil nickel-chrome
Diamètre du fil
(mm)
Section transversale
(mm2)
Surface par mètre
cm2/m
Cr20Ni80
Cr30Ni70
Cr15Ni60
Poids au mètre
kg/m
Résistance par mètre
Ω/m,20℃
Poids au mètre
kg/m
Résistance par mètre
Ω/m,20℃
Poids au mètre
kg/m
Résistance par mètre
Ω/m,20℃
0.10
0.007854
3.142
0.00006597
138.8
0.00006362
150.2
0.00006440
142.6
0.12
0.01131
3.770
0.00009500
96.38
0.00009161
104.3
0.00009274
99.03
0.15
0.01767
4.712
0.0001484
61.68
0.0001431
66.77
0.0001449
63.38
0.17
0.02270
5.341
0.0001907
48.02
0.0001839
51.99
0.0001861
49.34
0.19
0.02835
5.969
0.0002382
38.44
0.0002297
41.62
0.0002325
39.50
0.21
0.03464
6.597
0.0002909
31.47
0.0002806
34.07
0.0002840
32.34
0.25
0.04909
7.854
0.0004123
22.21
0.0003976
24.04
0.0004025
22.82
0.27
0.05726
8.482
0.0004809
19.04
0.0004638
20.61
0.0004695
19.56
0.29
0.06605
9.111
0.0005548
16.50
0.0005350
17.86
0.0005416
16.96
0.31
0.07548
9.739
0.0006340
14.44
0.0006114
15.63
0.0006189
14.84
0.35
0.09621
11.00
0.0008082
11.33
0.0007793
12.26
0.0007889
11.64
0.40
0.1257
12.57
0.001056
8.674
0.001018
9.390
0.001030
8.913
0.45
0.1590
14.14
0.001339
6.835
0.001288
7.419
0.001304
7.042
0.50
0.1963
15.71
0.001469
5.551
0.001590
6.010
0.001610
5.704
0.60
0.2827
18.85
0.002375
3.855
0.002290
4.173
0.002318
3.961
0.70
0.3848
21.99
0.003233
2.832
0.003117
3.066
0.003156
2.910
0.80
0.5027
25.13
0.004222
2.168
0.004072
2.348
0.004122
2.228
0.90
0.6362
28.27
0.005344
1.713
0.005153
1.855
0.005217
1.761
1.00
0.7854
31.42
0.006597
1.388
0.006362
1.502
0.006440
1.426
1.20
1.131
37.70
0.009500
0.9638
0.009161
1.043
0.009274
0.9903
1.40
1.539
43.98
0.01293
0.7081
0.01247
0.7665
0.01262
0.7276
1.60
2.011
50.27
0.01689
0.5421
0.01629
0.5869
0.01649
0.5570
1.80
2.545
56.55
0.02138
0.4283
0.02061
0.4637
0.02087
0.4401
2.00
3.142
62.83
0.02639
0.3470
0.02545
0.3756
0.02576
0.3565
2.20
3.801
69.12
0.03139
0.2867
0.03079
0.3104
0.03117
0.2946
2.50
3.976
70.69
0.03340
0.2741
0.03221
0.2968
0.03260
0.2817
2.80
6.158
87.96
0.05172
0.1770
0.04988
0.1916
0.05049
0.1819
3.00
7.069
94.25
0.05938
0.1542
0.05726
0.1669
0.05796
0.1584
3.50
9.621
110.0
0.08082
0.1133
0.07793
0.1226
0.07889
0.1164
4.00
12.57
125.7
0.1056
0.08674
0.1018
0.09390
0.1030
0.08913
4.50
15.90
141.4
0.1336
0.06853
0.1288
0.07419
0.1304
0.07042
5.00
19.63
157.1
0.1649
0.05551
0.1590
0.06010
0.1610
0.05704
5.50
23.76
172.8
0.1996
0.04588
0.1924
0.04967
0.1948
0.04714
6.00
28.27
188.5
0.2375
0.03855
0.2290
0.04173
0.2318
0.03961
6.50
33.18
204.2
0.2787
0.03285
0.2688
0.03556
0.2721
0.03375
7.00
38.48
219.9
0.3233
0.02832
0.3117
0.03066
0.3156
0.02910